Yield Strength: (0.2% Offset) 55 KSI min (380 MPA min) Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength: (0.2% Offset) 45 KSI min (310 MPA min) Ultimate Tensile Strength: 85 KSI min (585 MPA min) Ultimate Tensile Strength: 75 KSI min (515 MPa min) Yield Strength (0.2% Offset): 30 KSI min (205 MPa min) Elongation: 40% min Hardness: Rb 95 max Properties Tempered

Melting Range: 2500 - 2590 ☏ (1371 - 1421 ☌) FormsĬoil - Strip, Foil, Ribbon Wire - Profile, Round, Flat, Square Mechanical Properties of 316 Stainless Steel at Room Temperature Properties: Typical Magnetic Permeability: H = 200 Oersteds: Annealed < 1.02 max Mean Coefficient of Thermal Expansion: in/inl☏ (µm/m Thermal Conductivity: BTU/hr/ft2/ft/☏ (W/m Chemistry TypicalĬarbon: 0.08 max Manganese: 2.00 max Silicon: 1.00 max Chromium: 16.00-18.00 Nickel: 10.00-14.00 Molybdenum: 2.00-3.00 Phosphorus 0.040 Sulfur: 0.030 max Copper: 0.75 max Iron: Balance Physical Properties of 316 Stainless SteelĮlectrical Resistivity: microhm-in (microhm-cm): The low carbon version of 316 Stainless is 316L Stainless Steel which has increased resistance to intergranular corrosion. For instance, the 316 alloy may become magnetic when cold worked.Ĭorrosion resistance is improved, particularly against sulfuric, hydrochloric, acetic, formic and tartaric acids, as well as corrosion caused by acid sulfates and alkaline chlorides. While 316 can typically be drawn and formed in a similar fashion to 304, temperature variations can make those processes challenging. In regards to formability, 304 stainless is usually a better option for forming operations because the higher molybdenum content in Grade 316 means that it possesses higher strength and work-hardening rates which can have adverse effects on formability. Properties of this austenitic stainless steel grade are similar to those of type 304 except that type 316 is somewhat stronger at elevated temperature ranges. This addition increases corrosion resistance, improves resistance to pitting chloride ion solutions and provides increased strength at elevated temperatures. Type 316 (UNS 31600) is an austenitic chromium-nickel stainless steel alloy containing molybdenum.

Exterior Architectural components in Marine Coastal Areas.316 Stainless Steel Strip, Coil, Foil, Wire, ASTM A666, AMS5524 316 Stainless Steel Applications

316 stainless steel